Comparison between fracture mechanics and local approach models for the analysis of shallow cracks

Journal De Physique. IV : JP

Volumn 6, Issue 6, 1996, Pages

  Eisele, U ^a   Seidenfuss, M ^a   Pitard Bouet, J M ^b  

^a UNIVERSITY OF STUTTGART   (Germany)

^b EDF R AND D   (France)

Author keywords

[No Author keywords available]

Indexed keywords

BENDING (DEFORMATION); CALCULATIONS; CRACK INITIATION; CRACK PROPAGATION; FAILURE (MECHANICAL); FRACTURE MECHANICS; MANGANESE ALLOYS; MATHEMATICAL MODELS; NUMERICAL ANALYSIS; STRESSES;

LOCAL APPROACH MODEL; MANGANESE MOLYBDENUM NICKEL ALLOYS; ROUSSELIER MODEL; SHALLOW CRACKS; STRESS TRIAXIALITY;

CRACKS;

EID: 0030261688     PISSN: 11554339     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Review

References (27)

1. IC, a measure of fracture toughness.
2. EGF P1-90, EGF recommendations for determining the fracture resistance of ductile materials, European Group on Fracture, 1989.
3. Roos E., Eisele U.: Determination of the material characteristic values in the elastic-plastic fractue mechanics by means of J-integral crack resistance curves, Journal of Testing and Evaluation, Vol. 16 No.1, 1988.
4. Roos E., Eisele U.: Evaluation od different J-initiation values with regard to their usability in the safety assessment of components, Nuclear Engineering and Design 130, 1991.
5. Roos E., Seidenfuss M., Krämer D., Krolop S., Eisele U., Hindenlang U.: Application and evaluation of different numerical methods for determining crack resistance curves, Nuclear Engineering and Design 130, 1991.
6. Brocks W., Fricke S., Veith H.: Großes stabiles Rißwachstum in Bruchmechanikproben, 18th MPA-Seminar, 1992.
7. Roos E., Eisele U., Silcher H., Spaeth F.: The influence of the material toughness and the state of stress on fracture of large scale specimens, Nuclear Engineering and Design 102, 1987.
8. Eisele U., Roos E., Seidenfuss M., Silcher H.: Determination of J-integral-based crack resistance curves and initiation values for the assessment of cracked large scale specimens, Fracture Mechanics: 21nd symposium Vol. 1, ASTM STP 1131, 1992.
9. Clausmeyer H., Kussmaul K., Roos E.: Influence of stress state on the failure behavior of cracked components made of steel, Appl. Mech. Rev. Vol. 44 No. 2, 1991.
10. Beremin F. M.: Experimental and numerical study of the different stages in ductile rupture: application to crack initiation and stable crack growth, Three-dimensional constitutive relations and ductile fracture, North-Holland publishing company, 1981.
11. Rousselier G.: Ductile fracture models and their potential in local approach of fracture, Nuclear Engineering and Design 105, 1987.
12. Gurson , A.L.: Plastic flow and fracture behavior of ductile materials incorporating void nucleation, growth and interaction, PhD thesis, Division of Engineering, Brown University, Providence, R.I., June 1975
13. Tvergaard V.: Influence of voids on shear band instabilities under plane strain, Int. journal on fracture vol. 17, 1981.
14. Kussmaul K., Seidenfuss M., Eisele U.: On the applicability of damage models for the description of the failure behaviour of ductile steels ICF8 Conference, Kiev Ukraine, 1993.
15. Kussmaul K., Eisele U., Seidenfuss M.: On the applicability of local approach models for the determination of the failure behaviour of steels of different toughness, ASME PVP-Vol. 304, Fatigue and Fracture Mechanics in Pressure Vessel and Piping, 1995.
16. Sun D.-Z., Brocks W., Schmitt W.: Fracture toughness evaluation from tension and charpy type specimens based on micromechanical material models, ICF8 Conference, Kiev Ukraine, 1993.
17. Bethmont M., Rousselier G., Kussmaul K., Sauter A., Jovanovic A.: The method of "local approach" and its application to a thermal shock experiment, 14th MPA-Seminar, 1988.
18. Beremin F.M.: Numerical modelling of warm prestress effect using a damage function for cleavage fracture, ICF5 Conference, Cannes France, 1981.
19. Schmauder S.: Schädigungsmechanische Modellierung des mikrostrukturellen Versagens in Al/SiC-Verbundwerkstoffen, 28. Tagung DVM-Arbeitskreis >Bruchvorgänge<, Bremen Germany, 1996.
20. Arndi J., Dahl W.: Einfluß des Spannungszustandes auf die Mechanismen des Gleitbruchs, 28. Tagung DVM-Arbeitskreis >Bruchvorgänge<, Bremen Germany, 1996.
21. Kussmaul K., Seidenfuss M.: Experimental and numerical investigations to describe the failure behaviour of steels of different toughness by means of damage models, BMFT Reactor Safety Research - Project No. 1500 913, 1995.
22. Seidenfuss M.: Untersuchungen zur Beschreibung des Versagensverhaltens mit Hilfe von Schädigungsmodellen am Beispiel des Werkstoffes 20 MnMoNi 5 5, Dissertation an der Fakultät für Energietechnik der Universität Stuttgart, 1992.
23. Eisele U., Herter K.H., Schuler X.: Influence of the multiaxiality of stress state on the ductile fracture behaviour of degraded piping components, Proceedings of ECF 10, Berlin, 1994.
24. Clausmeyer H.: Über die Beanspruchung von Stahl bei mehrachsigen Spannungszuständen, Konstruktion 20 Heft 10, 1968.
25. Roos E., Eisele U., Silcher H.: Effect of stress state on the ductile fracture behavior of large scale specimens, ASTM Symposium on Constraint Effects in Fracture, ASTM 1171, 1993.
26. Schoch F.-W.: Eigenschaften formgeschweißter Großbauteile; Werkstoffuntersuchungen an einem 72t Versuchskörper aus Schweißgut 10 MnMoNi 5 5, Techn.-wiss. Ber. MPA Stuttgart, 1984.
27. Sprock A.: Numerische Untersuchungen lokaler und globaler Kriterien für die Initiierung von duktilen Bruchvorgängen, Berichte aus dem Institut für Eisenhüttenkunde RWTH Aachen, Band 2/95, 1995.