Overload retardation effects on stress corrosion behaviour of prestressing steel

Construction and Building Materials

Volumn 10, Issue 7, 1996, Pages 501-505

  Toribio, J ^a   Lancha, A M ^b  

^a UNIVERSITY OF A CORUÑA   (Spain)

^b CIEMAT   (Spain)

Author keywords

Overload retardation; Prestressing steel; Stress corrosion cracking

Indexed keywords

CRACK INITIATION; FATIGUE OF MATERIALS; FRACTURE MECHANICS; PRESTRESSED CONCRETE; RESIDUAL STRESSES; STRESS CORROSION CRACKING; STRUCTURAL LOADS;

CLEAVAGE LIKE FRACTURE MODE; OVERLOAD RETARDATION; TRANSITION TOPOGRAPHY;

STEEL STRUCTURES;

EID: 0030260557     PISSN: 09500618     EISSN: None     Source Type: Journal    
DOI: 10.1016/0950-0618(96)00015-3     Document Type: Article

References (14)

1. Broek, D. Elementary Engineering Fracture Mechanics, Martinus Nijhoff, The Hague, 1982
2. Barsom, J.M. and Rolfe, S.T. Fracture and Fatigua Control in Structures, Prentice-Hall, New Jersey, 1987
3. Suresh, S. Fatigue of Materials, Cambridge University Press, 1991
4. Jonas, O. Influence of preloading on the sustained load cracking behaviour of maraging steels in hydrogen. Corros. NACE 1973, 29, 299-304
5. Jonas, O. Effects of overload on hydrogen sulphide cracking. In Proc. Fourth Int. Conf. on Fracture - ICF4, Waterloo, Canada, June 1977, Vol. 2, pp. 269-277
6. Hanisch, A.H. and Burck, L.H. Effects of overloads on the incubation time for stress corrosion cracking of 7075 Aluminum. Corros. NACE 1982, 38, 330-335
7. Parkins, R.N. Slow strain rate testing 25 years experience. ASTM STP, 1993, 1210, 7-21
8. Parkins, R.N. Elices, M., Sánchez Gálvez, V. and Caballero, L. Environment sensitive cracking of prestressing steels, Corros. Sci. 1982, 22, 379-405
9. Slow Strain Rate Testing, ISO 7539-7, 1989
10. Rice, J.R. Mechanics of crack tip deformation and extension by fatigue. ASTM STP, 1967, 415, 247-309
11. Gortemaker, P.C.M., de Pater, C. and Spiering, R.M.E.J. Near-crack tip finite strain analysis. In Advances in Fracture Research (ICF5), ed. D. Francois, Pergamon, Oxford, 1981, pp. 151-160
12. Toribio, J., Lancha, A.M. and Elices, M. The tearing topography surface as the zone associated with hydrogen embrittlement processes in pearlitic steel. Metall. Trans. 1992, 23A, 1573-1584
13. Toribio, J. and Lancha, A.M. On the meaning of thresholds in environmentally assisted cracking. J. Mater. Sci. Lett. 1992, 11, 1085-1086
14. ISCC. (p). Scripta Metall. 1979, 13, 1057-1062