Effect of Halide Ions on Electrochemical Behavior and Stress Corrosion Cracking of 67/33 α-Brass in Aqueous Environments

Corrosion

Volumn 52, Issue 9, 1996, Pages 690-696

  Lee, C K ^a   Shih, H C ^a  

^a NATIONAL TSING HUA UNIVERSITY   (Taiwan)

Author keywords

Aqueous environments; Fractography; Halides; Inhibitors; Intergranular stress corrosion cracking; Open circuit potential; Potentiodynamic testing; Slow strain rate testing; Strain rate; brass

Indexed keywords

BRASS; CHEMICAL ANALYSIS; CORROSION INHIBITORS; CYCLIC VOLTAMMETRY; DISSOLUTION; ELECTROCHEMISTRY; FRACTOGRAPHY; HALOGEN COMPOUNDS; IONS; POLARIZATION; SOLUTIONS; STRAIN RATE;

AQUEOUS ENVIRONMENTS; ELECTROCHEMICAL POLARIZATION ANALYSIS; HALIDE IONS; INTERGRANULAR STRESS CORROSION CRACKING; OPEN CIRCUIT POTENTIAL; POTENTIODYNAMIC TESTING; SLIP DEALLOYING DISSOLUTION; SLOW STRAIN RATE TESTING;

STRESS CORROSION CRACKING;

EID: 0030244831     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3292159     Document Type: Article

References (42)

1. D.M. Brasher, Nature 193(1962): p. 862.
2. S.M. Mayanna, T.H.V. Setty, Corros. Sci. 14 (1974): p. 691.
3. M. Jesionek, Z. Szklarska-Smialowska, Corros. Sci. 23 (1983): p. 183.
4. M. Drogowska, L. Brossard, H. Menard, Surf. Coat. Technol. 34 (1988): p. 383.
5. D.A. Vermilyea, in Fundamental Aspects of Stress Corrosion Cracking, eds. R.W. Staehle, Forty, D. Van Rooyen (Houston, TX: NACE, 1969), p. 15.
6. M.O. Speidel, in The Theory of Stress Corrosion Cracking in Alloys, ed. J.C. Scully (Brussels, Belgium: 1971), p. 289.
7. T.R. Beck, in The Theory of Stress Corrosion Cracking in Alloys, ed. J.C. Scully (Brussels, Belgium: 1971), p. 64.
8. J.A. Feeney, M.J. Blackburn, in The Theory of Stress Corrosion Cracking in Alloys, ed. J.C. Scully (Brussels, Belgium: 1971), p. 355.
9. A. Kawashima, A.K. Agrawal, R.W. Staehle, in Stress Corrosion Cracking - The Slow Strain Rate Technique, ASTM STP 665 (Philadelphia, PA: ASTM, 1979), p. 266.
10. F. Zucchi, G. Trabanelli, G. Demertzis, Corros. Sci. 28 (1988): p. 69.
11. D.S. Tomalin, ASTM STP 633 (Philadelphia, PA: ASTM, 1977), p. 557.
12. D. Lee, R.B. Adamson, ASTM STP 633 (Philadelphia, PA: ASTM, 1977), p. 385.
13. K. Une, J. Nucl. Sci. Technol. 16 (1979): p. 660.
14. W.S. Ryu, J.Y. Lee, Y.H. Kang, H.C. Suk, J. Mater. Sci. 25 (1990): p. 3,167.
15. H. Uhlig, K. Gupta, W. Liang, J. Electrochem. Soc. 122 (1975): p. 343.
16. M. Kermani, J.C. Scully, Corros. Sci. 19 (1979): p. 89.
17. S.C. Sircar, U.K. Chatterjee, G.M. Sherbini, Corros. Sci. 23 (1983): p. 777.
18. S. Torchio, F. Mazza, Corros. Sci. 26 (1986): p. 813.
19. T.P. Hoar, C.J.L. Booker, Corros. Sci. 5 (1965): p. 821.
20. N.D. Greene, in Experimental Electrode Kinetics (Troy, NY: Rensselaer Polytechnic Institute, 1965).
21. ASTM G 49-85, "Preparation and Use of Direct Tension Stress Corrosion Test Specimens" (Philadelphia, PA: ASTM, 1985).
22. J. Congleton, H.C. Shih, T. Shoji, R.N. Parkins, Corros. Sci. 25 (1985): p. 769.
23. H.C. Shih, R.J. Tzou, J. Electrochem. Soc. 138 (1991): p. 958.
24. J.R. Galvele, in Passivity of Metals, eds. R.P. Frankenthal, J. Kruger (Pennington, NJ: The Electrochemical Society, 1978), p. 285.
25. S.A. Bradford, Corrosion 34 (1978): p. 96.
26. S.S. Birley, D. Tromans, Metall. T-A 12A (1981): p. 1,215.
27. J. Yu, N.J.H. Holroyd, R.N. Parkins, in Environment-Sensitive Fracture-Evaluation and Comparison of Test Methods, ASTM STP 821 (Philadelphia, PA: ASTM, 1984), p. 288.
28. J.A. Beavers, G.H. Koch, Corrosion 48 (1992): p. 256.
29. R.N. Parkins, in The Theory of Stress Corrosion Cracking in Alloys, ed. J.C. Scully, (Brussels, Belgium: 1971), p. 449.
30. H. Choi, F.H. Beck, Z. Szklarska-Smialowska, D.D. Macdonald, Corrosion 38 (1982): p. 76.
31. T.K.G. Namboodhiri, R.S. Tripathi, Corros. Sci. 26 (1986): p. 745.
32. A. Parthasarati, N.W. Polan, Corrosion 43 (1987): p. 747.
33. H.C. Shih, R.J. Tzou, Corros. Sci. 35 (1993): p. 479.
34. M. Pourbaix, in Altas of Electrochemical Equilibria in Aqueous Solutions (Houston, TX: NACE, 1974), p. 387.
35. D. Tromans, R.H. Sun, J. Electrochem. Soc. 138 (1991): p. 3,235.
36. I. Suzuki, Corros. Sci. 25 (1985): p. 1,029.
37. I. Suzuki, S. Wada, Corros. Sci. 27 (1987): p. 475.
38. R.N. Parkins, Corros. Sci. 20 (1980): p. 147.
39. T. Zakroczmski, R.N. Parkins, Corros. Sci. 20 (1980): p. 723.
40. R.C. Newman, K. Sieradzki, Scripta Metall. 17 (1983): p. 621.
41. R.C. Newman, G.T. Burstein, J. Electrochem. Soc. 127 (1980): p. 2,527.
42. K. Sieradzki, R.C. Newman, Phil. Mag. A. 51 (1985): p. 95.