High-temperature oxidation and hot corrosion behavior of two kinds of thermal barrier coating systems for advanced gas turbines

Journal of Thermal Spray Technology

Volumn 5, Issue 3, 1996, Pages 259-268

  Yoshiba, M ^a   Abe, K ^a   Aranami, T ^a,b   Harada, Y ^c  

^a TOKYO METROPOLITAN UNIVERSITY   (Japan)

^b IHI CORPORATION   (Japan)

^c TOCALO CO LTD   (Japan)

Author keywords

Ceramic coating; Failure analysis; High temperature oxidation; Hot corrosion; Thermal barrier coating system

Indexed keywords

CERAMIC COATINGS; COMPOSITION EFFECTS; CORROSION; FAILURE ANALYSIS; FUSED SILICA; GAS TURBINES; HIGH TEMPERATURE EFFECTS; LIME; OXIDATION; PLASMA SPRAYING; THERMAL INSULATING MATERIALS; ZIRCONIA;

THERMAL BARRIER COATING (TBC) SYSTEMS; THERMOCHEMICAL LOADINGS;

PROTECTIVE COATINGS;

EID: 0030243121     PISSN: 10599630     EISSN: None     Source Type: Journal    
DOI: 10.1007/BF02645876     Document Type: Article

References (13)

1. G.W. Meetham, Coating Requirements in Gas Turbine Engines, J. Vac. Sci. Technol., Vol A3 (No. 6), 1985, p 2509-2515
2. H. Takeda, Ceramic Coating, H. Takeda, Ed., Nikkan-Kogyo-Shimbunsya, Tokyo, 1988, p 179-199 (in Japanese)
3. S.R.J. Saunders and J.R. Nicholls, Coatings and Surface Treatments for High Temperature Oxidation Resistance, Mater. Sci. Technol., Vol 5, 1989, p 780-798
4. S. Sodeoka, M. Suzuki, T. Inoue, Y. Ono, and K. Ueno, Plasma Spray under Controlled Atmosphere up to 300 kPa, Proc. ITSC '95, A. Ohmori, Ed., High Temp. Soc. Japan, Vol 1, 1995, p 283-288
5. P.E. Hodge, R.A. Miller, and M.A. Gedwill, Evaluation of the Hot Corrosion Behavior of Thermal Barrier Coatings, Thin Solid Films, Vol 73, 1990, p 447-453
6. R. Tanaka and O. Miyagawa, Test Methods for Fuel Oil Ash Corrosion of Heat Resisting Alloys, Trans. ASME-JEMT, Vol 10, 1973, p 322-329
7. M. Yoshiba, O. Miyagawa, H. Mizuno, and H. Fujishiro, Effect of Environmental Factors on the Creep Rupture Properties of a Nickel-Base Superalloy Subjected to Hot Corrosion, Trans. Japan Inst. Metals, Vol 29, 1988, p 26-41
8. K. Wada, M. Yoshiba, and Y. Harada, Failure and Strength Degradation in Hot Corrosion Environment of Various Nickel-Base Superalloy/Coating Systems by Plasma Spraying, Rep. 123rd Committee of Japan Soc. Promotion Sci., Vol 32, 1991, p 405-425 (in Japanese)
9. M. Yoshiba, Effect of Hot Corrosion on the Mechanical Performances of Superalloys and Coating Systems, Corros. Sci., Vol 35, 1993, p 1115-1124
10. M. Yoshiba, T. Aranami, H. Taira, and Y. Harada, Failure Analysis of Some Plasma Spray Coated Superalloy Systems Subjected to the Synergistic High Temperature Damage in Actual Gas Turbine or in Laboratory, Proc. ITSC '95, A. Ohmori, Ed., High Temp. Soc. Japan, Vol 1, 1995, p 89-94
11. B.C. Wu and E. Chang, Thermal Cyclic Response of Yttria-Stabilized Zirconia/CoNiCrAlY Thermal Barrier Coatings, Thin Solid Films, Vol 172, 1989, p 185-196
12. S. Stecura, Effects of Yttrium, Aluminum and Chromium Concentrations in Bond Coatings on the Performance of Zirconia-Yttria Thermal Barriers, Thin Solid Films, Vol 73, 1980, p 481-489
13. S. Stecura, Two-Layer Thermal Barrier Coatings, Part I: Effects of Composition and Temperature on Oxidation Behavior and Failure, Thin Solid Films, Vol 182, 1989, p 121-139