The effect of microstructure on fracture mechanisms of 2·25Cr1Mo low alloy steel, part A: The influence of non-metallic inclusions

International Journal of Pressure Vessels and Piping

Volumn 67, Issue 3, 1996, Pages 317-327

  Norris, S D ^a   Parker, J D ^a  

^a SWANSEA UNIVERSITY   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

BENDING (DEFORMATION); DUCTILITY; FAILURE (MECHANICAL); FRACTOGRAPHY; FRACTURE MECHANICS; INCLUSIONS; MATERIALS TESTING; METALLOGRAPHIC MICROSTRUCTURE; STRAIN; THERMAL EFFECTS;

BEND TESTING; CLEAVAGE; DUCTILE VOIDS;

STEEL;

EID: 0030217799     PISSN: 03080161     EISSN: None     Source Type: Journal    
DOI: 10.1016/0308-0161(94)00000-X     Document Type: Article

References (13)

1. Conrad, H. & Hayes, W. Thermally activated deformation of the BCC metals at low temperatures, Transactions of the ASM, 56 (1963) 249.
2. Argon, A. S., Im, J. & Safoglu, R., Cavity formation from inclusions in ductile fracture, Met. Trans., 6a (1975) 825.
3. Goods, S. H. & Brown, L. M., The nucleation of cavities by plastic deformation, Acta Met., 27 (1979) 1.
4. Ritchie, R. O., Smith, R. F. & Knott, J. F., Effects of thickness on fibrous fracture from a notch and on fatigue-crack propagation in low-strength steel, Metal Science, 9 (1975) 485.
5. Knott, J. F., Micromechanisms of fibrous crack extension in engineering alloys, Metal Science (August 1980) 327.
6. McMahon, C. J. & Cohen, M., Initiation of cleavage in polycrystalline iron, Acta Met., 13 (June 1965) 591.
7. Lindley, T. C., Oates, G. & Richards, C. E., A critical appraisal of carbide cracking mechanisms in ferride/carbide aggregates. Acta Met., 18 (November 1970) 1127.
8. Knott, J. F., Some effects of hydrostatic tension on the fracture behaviour of mild steel, J. Iron Steel Inst., (February 1966) 104.
9. Rice, J. R. & Johnson, M. A., in Inelastic Behaviour of Solids, McGraw Hill, New York (1970) 641-649.
10. Tweed, J. H. & Knott, J. F.. Micromechanisms of Failure in C-Mn Weld Metals. Acta Met., 35 (1987) 1401.
11. Baik, J. M., Kameda, J. & Buck, O., Development of small punch tests for ductile-brittle transition temperature measurement of temper embrittled Ni-Cr steels, in The Use of Small Scale Specimen Testing for Irradiated Material, ASTM, Philadelphia, (1986) 92.
12. Manahan, M. P., Browning, A. E., Argon, A. S. & Harling, O. K., Miniaturised disk bend test technique development and application, The Use of Small Scale Specimen Testing for Irradiated Material, ASTM, Philadelphia. (1986) 17.
13. Norris, S. D. & Parker, J. D., The effect of microstructure on fracture mechanisms of 2·25Cr1Mo low alloy steel: part B the influence of carbides, Int. J. Pressure Vessels Piping, 67 (1996) 329.