Environment-Induced Deformation Localization during Transgranular Stress Corrosion Cracking

Corrosion (Houston)

Volumn 52, Issue 5, 1996, Pages 347-355

  Lian, K ^b   Meletis E I ^a  

^a LOUISIANA STATE UNIVERSITY   (United States)

^b NONE

Author keywords

Brass; Cleavage; Crack initiation; Crack patterning; Crack propagation; Deformation patterning; Dislocations; Dissolution; Plastic deformation; Slip bands; Slip localization; Stress corrosion cracking; Surface plasticity; Transgranular cracking; Vacancies

Indexed keywords

BRASS; CRACK INITIATION; CRACK PROPAGATION; DISLOCATIONS (CRYSTALS); DISSOLUTION; EMBRITTLEMENT; ENVIRONMENTAL IMPACT; FRACTURE; NUCLEATION; PLASTIC DEFORMATION; PLASTICITY; STRAIN;

CLEAVAGE; CRACK PATTERNING; DEFORMATION PATTERNING; ENVIRONMENT INDUCED DEFORMATION; SLIP BANDS; SLIP LOCALIZATION; SURFACE PLASTICITY; TRANSGRANULAR CRACKING; VACANCIES;

STRESS CORROSION CRACKING;

EID: 0030141568     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3292122     Document Type: Article

References (42)

1. Fundamental Aspects of Stress Corrosion Cracking, eds. S. Bruemmer, E.I. Meletis (Warrendale, PA: TMS-AIME, 1992).
2. Corrosion-Deformation Interactions, eds. T. Magnin, J.M. Gras (Les Ulis, France: Les Editions de Physique, 1993).
3. E.N. Pugh, Corrosion 41, 9 (1985): p. 517.
4. E.I. Meletis, R.F. Hochman, Corros. Sci. 24 (1984): p. 843.
5. E.I. Meletis, R.F. Hochman, Corrosion 40, 1 (1984): p. 39.
6. E.I. Meletis, R.F. Hochman, Corros. Sci. 26 (1985): p. 63.
7. S. Jani, M. Marek, R.F. Hochman, E.I. Meletis, Metall. Trans. 22A (1991): p. 1,453.
8. R.C. Newman, K. Sieradzki, Scrip. Metall. Mater. 17 (1983): p. 621.
9. E.I. Meletis, K. Lian, W. Huang, "Vacancy-Dislocation Interactions and Transgranular Stress Corrosion Cracking," Proc. Int. Conf. Corrosion-Deformation Interactions (Les Ulis, France: Les Editions de Physique, 1993), p. 69.
10. E.I. Meletis, K. Lian, J. Mech. Behav. Mater. 6 (1995): p. 69.
11. J.D. Eshelby, F.C. Frank, F.R.N. Nabarro, Philos. Mag. 42 (1951): p. 351.
12. J. Yu, R.N. Parkins, Y. Xu, G. Thompson, G.C. Wood, Corros. Sci. 27, 2 (1987): p. 141.
13. T. Magnin, R. Chieragatti, R. Oltra, Acta Metall. Mater. 38 (1990): p. 1,313.
14. W.F. Flanagan, P. Bastias, B.D. Lichter, Acta Metall. Mater. 39 (1991): p. 695.
15. A. Parthasarathi, N.W. Polan, Metall. T-A 13A (1982): p. 2,027.
16. D. McLean, J. Inst. Met. 80 (1951-1952): p. 507.
17. I.R. Kramer, B. Wu, C.R. Feng, Mater. Sci. Eng. 82 (1986): p. 141.
18. C.F. Lo, W.E. Mayo, S. Weissmann, CORROSION/88, paper no. 282 (Houston, TX: NACE, 1988).
19. K. Kamachi, T. Otsu, S. Abayashi, Trans. Jpn. Inst. Met. 35 (1971): p. 64.
20. D.B. Kasul, C.L. White, L.A. Heldt, "Relationships Between Plasticity and Stress Corrosion Cracking," Proc. Conf. Environment-Induced Cracking of Metals (Houston, TX: NACE, 1990), p. 219.
21. I.R. Kramer, C.R. Feng, B. Wu, Mater. Sci. Eng. 80 (1986): p. 37.
22. R.N. Pangborn, S. Weissmann, I.R. Kramer, Metall. Trans. 12A (1981): p. 109.
23. I.R. Kramer, S. Weissmann, Proc. Symp. Novel Non-Destructive Evaluation Methods for Materials (Warrendale, PA: TMS-AIME, 1982), p. 141.
24. S.E. Harvey, P.G. Marsh, W.W. Gerberich, Acta Metall. Mater. 42, 10 (1994): p. 3,493.
25. A.N. Stroh, Proc. Roy. Soc. 223 (1954): p. 404.
26. W.F. Flanagan, M. Wang, M. Zhu, B.D. Lichter, Metall. T-A 25A (1994): p. 1,391.
27. Li Shiqiong, J.I. Dickson, J.P. Baïlon, D. Tromans, Mater. Sci. Eng. A119 (1989): p. 59.
28. J.I. Dickson, Li Shiqiong, J.-P. Baïlon, D. Tromans, ̈The Fractography of Transgranular SCC in FCC Metals: Mechanistic Implications,̈ Proc. Symp. Fundamental Aspects of Stress Corrosion Cracking (Warrendale, PA: TMS-AIME, (1992), p. 303.
29. S.P. Lynch, Acta Metall. Mater. 29 (1981): p. 325.
30. C.D. Beachem, Metall. Trans. 3 (1972): p. 437.
31. H.K. Birnbaum, ̈Hydrogen-Related Failure Mechanisms in Metals,̈ Proc. Conf. Environment-Sensitive Fracture of Engineering Materials (Warrendale, PA: TMS-AIME, 1979), p. 326.
32. E.I. Meletis, W. Huang, Mater. Sci. Eng. A148 (1991): p. 197.
33. K. Sieradzki, R.C. Newman, Philos. Mag. A 51 (1985): p. 95.
34. D.A. Jones, Metall. T-A 16A (1985): p. 1,133.
35. J.R. Galvele, Corros. Sci. 27 (1987): p. 1.
36. T.R. Pinchback, S.P. Clough, L.C. Heldt, Metall. T-A 6A (1975): p. 1,479.
37. T.R. Pinchback, S.P. Clough, L.C. Heldt, Metall. T-A 7A (1976): p. 1,241.
38. D.A. Jones, A.F. Jankowski, Scrip. Metall. Mater. 29 (1993): p. 701.
39. I. Kramer, Trans. Metall. 6 (1964): p. 991.
40. R.H. Revie, H.H. Uhlig, Acta Metall. 2 (1974): p. 619.
41. W.W. Gerberich, S.K. Venkataraman, H. Huang, S.E. Harvey, D.L. Kohlstedt, Acta Metall. Mater. 43, 4 (1995): p. 1,569.
42. R. Armstrong, I. Codd, R.M. Douthwalte, Philos. Mag. 7, (1962): p. 45.