Volumn 44, Issue 3, 1996, Pages 863-871
|
An experimental study of the mechanisms of crack extension along an oxide/metal interface
a b |
Author keywords
[No Author keywords available]
|
Indexed keywords
BOND STRENGTH (MATERIALS);
DEFECTS;
DEFORMATION;
FAILURE (MECHANICAL);
FRACTURE;
GOLD;
INTERFACES (MATERIALS);
MATERIALS TESTING;
SAPPHIRE;
SEPARATION;
STRESS CORROSION CRACKING;
BLUNTING DISPLACEMENT;
BOND SEPARATION;
CRACK EXTENSION;
FRACTURE ENERGY;
INTERFACE FAILURE;
INTERFACIAL DECOHESION;
INTERFACIAL DEFECTS;
PLASTIC BLUNTING;
RESISTANCE CURVE;
SLIP PLANES;
CRACK PROPAGATION;
|
EID: 0030105829
PISSN: 13596454
EISSN: None
Source Type: Journal
DOI: 10.1016/1359-6454(95)00256-1 Document Type: Article |
Times cited : (70)
|
References (25)
|