Fracture mechanical behavior of aggregate-cement matrix interfaces

Journal of Materials in Civil Engineering

Volumn 7, Issue 4, 1995, Pages 199-203

  Tschegg, E K ^a   Rotter, H M ^a   Roelfstra, P E ^b   Bourgund, U ^c   Jussel, P ^d  

^a VIENNA UNIVERSITY OF TECHNOLOGY   (Austria)

^b Intron SME ^*  (Switzerland)

^c Hilti AG   (Liechtenstein)

^d Hilti Corporation   (Liechtenstein)

Author keywords

[No Author keywords available]

Indexed keywords

CEMENTS; CONCRETE AGGREGATES; CONCRETE TESTING; CRACK PROPAGATION; FRACTURE MECHANICS; FRACTURE TESTING; INTERFACES (MATERIALS); LOADS (FORCES); NONMETALLIC MATRIX COMPOSITES; SURFACES;

CEMENT-AGGREGATE INTERFACES; FRACTURE ENERGY; LOAD DISPLACEMENT CURVES; WEDGE SPLITTING TESTS;

CONCRETES;

EID: 0029410931     PISSN: 08991561     EISSN: None     Source Type: Journal    
DOI: 10.1061/(ASCE)0899-1561(1995)7:4(199)     Document Type: Article

References (19)

1. Aicher, S., and Reinhardt, H. W. (1993). “Einfluβ der BauteilgrÖβe in der linearen und nichtlinearen Holzbruchmechanik.” Holz als Roh- und Werkstoff, Berlin, Germany, 51, 215-220.
2. Bažant, Z. P. (1984). “Size effect in blunt fracture: concrete, rock, metal.” J. Engrg. Mech., ASCE, 110(4), 518-535.
3. Brameshuber, W., and Hilsdorf, K. H. (1990). “Influence of ligament length and stress state on fracture energy of concrete.” Engrg. Fracture Mech., 10, 148-156.
4. Hillemeier, B. (1976). “Bruchmechanische Untersuchungen des Riβfortschritts in zementgebundenen Werkstoffen,” PhD thesis, Univ. of Karlsruhe, Germany (in German).
5. Hillerborg, A., Modeer, M., and Peterson, P. E. (1976). “Analysis of formation and crack growth in concrete by means of fracture mechanics and finite elements.” Cement and Concrete Res., 6, 773-782.
6. Hsu, T. T. C., and Slate, F. O. (1963). “Tensile bond strength between aggragate and cement paste of mortar.” J. Am. Concrete Inst., 60(4), 465-486.
7. Larbi, J. A. (1993). Microstructure of the interfacial zone around aggregate particles in concrete, 38(1), TNO Build, and Constr. Res., Dept, of Build. Technol., Rijswijk, Heron, The Netherlands.
8. Malvar, L. J., and Warren, G. E. (1988). “Fracture energy for the three- point-bending tests on single-edge-notched beams.” Experimental Mech., (Sept.), 266-272.
9. “RILEM draft recommendation (50-FMC, 1985): Determination of the fracture of mortar and concrete by means of three-point bend tests on notched beams.” (1985). Mat. and Struct., 18, 287-290.
10. Roelfstra, P. E. (1988). “Numerical concrete,” PhD thesis, ETH Lausanne, Switzerland.
11. Sakai, M., and Inagaki, M. (1989). “Dimensionless load-displacement relation and its application to crack propagation problems.” J. Am. Ceramic Soc., 72(3), 388-394.
12. Sih, G., Paris, P. C., and Irwin, G. R. (1965). “On cracks in rectilineary anisotropic bodies using singular isoparametric elements.” Int. J. Fracture Mech., 1, 189-203.
13. Suga, T., and Elssner, G. (1985). “Haftfestigkeitsbestimmung an Ker- amik-Metall-Verbindungen mit Hilfe von Schichtverbundproben.” Z. Werkstofftech, 16, 75-80 (part 1), 122-125 (part 2), (in German).
14. Tschegg, E. K. (1991). “New equipment for fracture tests on concrete.” Mat. Testing (Materialprüfung), Berlin, Germany, 33, 338-342.
15. Tschegg, E. K., and Stanzl, S. E. (1991). “Adhesive power measurements of bonds between old and new concrete.” J. Mat. Sci., 26, 5189-5194.
16. Tschegg, E. K., Kirchner, H. O. K., and Kocak, M. (1990). “Cracks at the Ferrite-Austenite interfaces.” Acta Metallurgica & Materialia, 38(3), 469-478.
17. Tschegg, E. K., Kirchner, H. O. K., and Schwalbe, K.-H. (1993a). “Cracks at interfaces of different cohesion.” Acta Metall. & Mat., 41(9), 2783-2790.
18. Tschegg, E. K., Stanzl-Tschegg, S. E., and Litzka, J. (1993b). “New testing method to characterize mode I fracturing of asphalt aggregate mixtures.” Proc., 2nd RILEM Conf., “Reflective Cracking in Pavements,” C.R.R., J. M. Rigo, R. Degeimbre, and L. Francken, eds., F&FN Spon, London, England, 263-270.
19. Tschegg, E. K., Elser, M., and Kreuzer, H. (1994). “Mode I fracture behavior of concrete under biaxial loading.” J. Mat. Sci., 30, 235-242.