Improving the delamination resistance of CFRP by stitching-a review

Composites Science and Technology

Volumn 50, Issue 3, 1994, Pages 305-317

  Dransfield, Kimberley ^a   Baillie, Caroline ^a   Mai, Yiu Wing ^a  

^a UNIVERSITY OF SYDNEY   (Australia)

Author keywords

carbon fibre; composite; delamination; epoxy resin; impact; stiching

Indexed keywords

COMPOSITE MATERIALS; FATIGUE OF MATERIALS; MECHANICAL VARIABLES MEASUREMENT; PRESSURE MEASUREMENT; VISION;

CARBON FIBRE; DELAMINATION; EPOXY RESIN; RESISTANCE IMPROVEMENT; VELOCITY IMPACT LOADING;

STRUCTURAL DESIGN;

EID: 0028256905     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/0266-3538(94)90019-1     Document Type: Article

References (61)

1. Fracture behaviour in stitched multidirectional composites
2. Delamination resistance in stitched and unstitched composite planes subjected to composite loading
3. The impact resistance of composite materials—A review
4. Mechanical properties in multidimensional composites
5. The role of impact damage in post-impacted compression testing
6. Delamination resistance of stitched thermoplastic matrix composite laminates
7. 2·5D and 3D fabrics for delamination resistant composite laminates and sandwich structure
8. Tensile and shear properties of composites by various reinforcement concepts
9. Design approaches for edge delamination resistance in laminated composites
10. Stitching to improve damage tolerance of composites
11. Delamination if composite materials
12. Edge delamination resistance by a critical ply termination
13. Fracture at bimaterial interfaces: The role of residual stresses
14. An experimental study of the fracture resistance of bimaterial interfaces
15. Residual stress in 3D carbon/carbon composites
16. Delamination arrester—An adhesive inner layer in laminated composites
17. Edge effects and delamination failures
18. Improvement of edge delamination strength of composite laminates using adhesive layers
19. Impact-induced delamination—A view of bending stiffness mismatch
20. Toughness properties of a three dimensional carbon/epoxy composite
21. Mechanical properties and interlaminar toughness of cross-plied laminates containing adhesive strips
22. Impact resistance of fibre composites: Energy absorbing mechanisms and environmental effects
23. Modelling of compression after impact strength of advanced fibre composites
24. Cross reinforcement in a GR/EP laminate
25. The use of stitching to suppress delamination in laminated composites
26. Tensile strength of stitching joint in woven glass fabrics
27. The effect of stitching on in-plane and interlaminar properties of carbon/epoxy fabric laminates
28. Structural stitching of textile preforms
29. Delamination buckling with bridging
30. Buckling of delaminated composites re-examined
31. Experimental evaluation of the effect of stitching CFRP laminate specimen with various shapes and loadings
32. Compression response of thick layer composite laminates with through-the-thickness reinforcement
33. Damage tolerant composite materials produced by stitching carbon fibres
34. Removal of surface loop from stitched composites can improve compression and compression-after-impact strengths
35. Geometrical effects in the low velocity impact response of CFRP
36. Impact resistance of carbon fibre reinforced plastics
37. Impact response of tough carbon fibre composites
38. Rate effects on delamination fracture toughness of a toughened graphite/epoxy
39. High strength, high fracture toughness fibre composites with interface control—A review
40. Failure mechanism discrimination in carbon fibre reinforced epoxy composites
41. Influence of fibre/matrix interfacial adhesion on composite behaviour
42. The failure of fibre composites: An overview
43. Effect of graphite fibre/epoxy matrix on composite fracture behaviour
44. The effect of matrix modulus on lamina compression strength
45. Material characterization for matrix-dominated failure modes
46. The detailed structure of delamination fracture surfaces in graphite/epoxy laminates
47. Deformation and failure mechanisms in 3D composites
48. Mechanisms of compressive failure in 3D composites
49. Failure mechanisms in continuous carbon fibre reinforced PEEK composites
50. A new high performance resin system for RTM of aerospace structures
51. On-line in-situ control of the RTM process
52. A study of the mold filling process in RTM
53. A new high temperature epoxy system for RTM application
54. Multiaxial stitched preform reinforcement for RTM fabrication
55. Effect of process variables on the quality of RTM mouldings
56. Calculation of cure process variables during cure of graphite/epoxy composites
57. Control of composite cure processes
58. Ultimate glass transition temperature of thermoset resins and curing history