A new damage mechanics criterion for ductile fracture

Engineering Fracture Mechanics

Volumn 27, Issue 4, 1987, Pages 371-378

  Wei Hua Tai, ^a   Bing Xian Yang, ^a  

^a BEIHANG UNIVERSITY   (China)

Author keywords

[No Author keywords available]

Indexed keywords

MATERIALS - PHYSICAL PROPERTIES; MATHEMATICAL MODELS; SOLIDS - INCLUSIONS;

DAMAGE MECHANICS PARAMETER; DUCTILE FRACTURE; SUCCESSIVE DAMAGE PROCESSES;

FRACTURE MECHANICS;

EID: 0023251730     PISSN: 00137944     EISSN: None     Source Type: Journal    
DOI: 10.1016/0013-7944(87)90174-3     Document Type: Article

References (12)

1. Experimental and numerical study of the different stages in ductile rupture: Application to crack initiation and stable crack growth
2. A new microvoid-damage model for ductile fracture
3. On the influence of stress on ductile failure initiation in high strength steels
4. A plastic-strain, mean-stress criterion for ductile fracture
5. A criterion for ductile fracture by the growth of holes
6. On the ductile enlargement of voids in triaxial stress fields
7. Methodology and applications of local criteria for the prediction of ductile tearing
8. The correlation of triaxial state of stress and the failure strain
9. On the mechanisms of ductile failure in high-strength steel subjected to multi-axial stress-states
10. A continuous damage mechanics model for ductile fracture
11. Interpretation of ductile fracture toughness temperature dependence of a low strength steel in terms of a local approach
12. Crack initiation and stable crack growth resistance in A508 steels in relation to inclusions distribution