International Journal of Fracture

Volumn 9, Issue 3, 1973, Pages 277-293

The kinetics of subcritical crack growth under sustained loading

(2) Landes, J D a Wei, R P b

a Westinghouse Research & Development Cent (United States)

b LEHIGH UNIVERSITY (United States)

Author keywords

[No Author keywords available]

Indexed keywords

STEEL HEAT TREATMENT - TEMPERING;

SUBCRITICAL CRACKS;

STEEL TESTING;

EID: 0015661857 PISSN: 03769429 EISSN: 15732673 Source Type: Journal
DOI: 10.1007/BF00049196 Document Type: Article

Times cited : (53)

References (41)

1
- 0001368224
- Delayed Fracture of Metals under Static Load
- (1952) Nature , vol.169 , pp. 842-843
- Petch, N.J.¹ Stables, P.²

2
- 0004979710
- Transgranular Stress Corrosion in Chromium-Nickel Stainless Steels
- (1953) Journal of the Iron and Steel Institute , vol.173 , Issue.1 , pp. 140-146
- Edeleanu, C.¹

3
- 0001627155
- Hydrogen Crack Initiation, and Delayed Failure in Steel
- (1958) Transactions of the Metallurgical Society of AIME , vol.212 , pp. 528-536
- Johnson, H.H.¹ Morlet, J.G.² Troiano, A.R.³

4
- 84932593997
- Solid-Fuel Rocket Chambers for Operation at 240,000 psi and Above
- (1959) Metal Progress , vol.76 , Issue.5 , pp. 74-81
- Shank, M.E.¹ Spaeth, C.E.² Cooke, V.W.³ Coyne, J.E.⁴

5
- 3743051861
- Discontinuous Crack Growth in Hydrogenerated Steel
- (1959) Trans. of the Metallurgical Society of AIME , vol.215 , pp. 1048-1052
- Steigerwald, E.A.¹ Schaller, F.W.² Troiano, A.R.³

6
- 0008694949
- Stress Corrosion of Steels for Aircrart and Missiles
- (1960) Corrosion , vol.16 , Issue.264 , pp. 325t-335t
- Phelps, E.H.¹ Loginow, A.W.²

7
- 84932504055
- Crack Growth During Static Tests of Rocket Motor Cases
- (1960) Metal Progress , vol.78 , Issue.2 , pp. 79-82
- Bernstein, H.¹ Kies, J.A.²

8
- 84910269841
- Delayed Failure of High-Strength Steel in Liquid Environments
- (1960) Proceedings ASTM , vol.60 , pp. 750-760
- Steigerwald, E.A.¹

9
- 0542388816
- Evidence for an Electrochemical-Mechanical Stress Corrosion Fracture in a Stainless Steel
- (1965) Corrosion Science , vol.5 , Issue.10 , pp. 729-730
- Logan, H.L.¹ McBee, M.L.² Kaham, O.J.³

10
- 84932516208
- Elevated Temperature Stress Corrosion Resistance of Titanium Alloys
- (1965) Corrosion , vol.21 , Issue.10 , pp. 307-315
- Newcomer, R.¹ Tourkakis, H.C.² Turner, H.C.³

11
- 6244236146
- A Mechanism for the Embrittlement of High-Strength Steels by Aqueous Environments
- (1964) Transactions of the ASM , vol.57 , pp. 658-671
- Hanna, G.L.¹ Troiano, A.R.² Steigerwald, E.A.³

12
- 0001222528
- Hydrogen, Oxygen and Sub-critical Crack Growth in a High-Strength Steel
- (1966) Trans. AIME , vol.236 , Issue.4 , pp. 513-516
- Hancock, G.G.¹ Johnson, H.H.²

13
- 0010280850
- A Study of the Stress Factor in Corrosion Cracking by Use of the Pre-cracked Cantilever Beam Specimen
- (1965) Corrosion Science , vol.5 , Issue.11 , pp. 745-750
- Brown, B.F.¹ Beachem, C.D.²

14
- 79751534478
- Stress-Corrosion Susceptibility of High-Strength Steel, in Relation to Fracture Toughness
- (1966) Journal of Basic Engineering , vol.88 , pp. 777-782
- Mulherin, J.J.¹

15
- 0242265819
- Moisture and Stable Crack Growth in a High Strength Steel
- (1965) Applied Materials Research , vol.4 , pp. 34-40
- Johnson, H.H.¹ Willner, A.M.²

16
- 0014611879
- Environmentally Assisted Fatigue Crack Growth Rates in SAE 4340 Steel
- (1969) Journal of Basic Engineering , vol.91 , pp. 598-602
- Gallagher, J.P.¹ Sinclair, G.M.²

17
- 4243146683
- A Study of Stress-Corrosion Cracking by Wedge-Force Loading
- (1969) Engineering Fracture Mechanics , vol.1 , pp. 123-128
- Smith, H.R.¹ Piper, D.E.² Downey, F.K.³

18
- 0542365114
- Mechanisms of Environment Induced Sub-critical Flaw Growth in AISI 4340 Steel
- (1969) Engineering Fracture Mechanics , vol.1 , pp. 447-462
- Van Der Sluys, W.A.¹

19
- 84932513509
- Fracture Mechanics and Stress Corrosion
- (1969) Materials and Metals , vol.3 , Issue.5 , pp. 174-175
- Scully, J.C.¹

20
- 36949054879
- Rate-controlling Step in Stress Corrosion Cracking
- (1968) Nature , vol.218 , pp. 1156
- Ugiansky, G.M.¹ Skolnick, L.P.² Kruger, J.³ Steifel, S.W.⁴

21
- 84932576636
- G. R. Irwin, Fracture; Handbuch der Physik, Vol. VI, Springer, (1958).

22
- 0014587482
- The Effect of Silicon on the Stress-Corrosion Resistance of Low-Alloy High-Strength Steels
- (1969) Corrosion , vol.25 , Issue.10 , pp. 423-431
- Carter, C.S.¹

23
- 84932577701
- S. Mostovoy, H. R. Smith, R. G. Lingwall and E. J. Ripling, A Note on Stress Corrosion Cracking Rates, Materials Research Laboratory, Inc.

24
- 0014763343
- Some Aspects of Environment-Enhanced Fatigue-Crack Growth
- (1970) Engineering Fracture Mechanics , vol.1 , pp. 633-651
- Wei, R.P.¹

25
- 84932544170
- W. F. Brown, Jr. and J. E. Srawley, Plane Strain Crack Toughness Testing of High-Strength Metallic Materials, ASTM, STP 410, American Society for Testing and Materials (1966).

26
- 84932583980
- Isida, Crack Tip Stress Intensity Factors for the Tension of an Eccentrically Cracked Strip, Lehigh University, Department of Mechanics Report. 1965.

27
- 84932515434
- J. E. Srawley and B. Gross, Stress Intensity Factors for Crackline-Loaded Edge-Crack Specimens, NASA Technical Note D-3820, (1967).

28
- 84932594161
- J. E. Srawley and W. F. Brown, Jr., Fracture Toughness Test Methods, Fracture Toughness Testing and Its Applications, ASTM STP 381, American Society for Testing and Materials (1965) 133.

29
- 11644262069
- Diffusion of Hydrogen from Water Through Steel
- (1940) Journal of Applied Physics , vol.11 , pp. 262-267
- Norton, F.J.¹

30
- 0012374049
- (1960) Transactions of the Metallurgical Society of AIME , vol.218 , pp. 1104
- Johnson, F.W.¹ Hill, M.H.²

31
- 84932507113
- H. L. Eschbach, F. Gross and S Schlien, Permeability Measurements with Gaseous Hydrogen for Various Steels, Vacuum, 13, 543–547.

32
- 0040336046
- The Diffusion of Hydrogen in Steel at Temperatures of-78°C to 200°C
- (1958) Journal of the Iron and Steel Institute , vol.189 , Issue.2 , pp. 315-321
- Hobson, J.D.¹

33
- 36849135780
- Hydrogen Permeation Through Steel During Abrasion
- (1957) Journal of Applied Physics , vol.28 , pp. 380
- Frank, R.L.¹ Swets, D.E.²

34
- 84932522213
- R. Hewitt, Iron and Steel Institute, Special Report 73.

35
- 0001057127
- Hydrogen Permeation in Metals as a Function of Stress, Temperature, and Dissolved Hydrogen Concentration
- (1966) Proceedings of the Royal Society A: Mathematical, Physical and Engineering Sciences , vol.290 , Issue.1421 , pp. 220-235
- Beck, W.¹ Bockris, J. O'M.² McBreen, J.³ Nanis, L.⁴

36
- 78751615298
- The Role of Surface Stress on Hydrogen Absorption by 4340 Steel
- (1968) Corrosion , vol.24 , Issue.8 , pp. 243-246
- Phalen, D.I.¹ Vaughan, D.A.²

37
- 0014710313
- Embrittlement of 4130 Steel by Low-Pressure Gaseous Hydrogen
- (1970) Metallurgical Transactions , vol.1 , pp. 63-68
- Willia, D.P.¹ Nelson, H.G.²

38
- 0001753683
- Calibrating the Electric Potential Method for Studying Slow Crack Growth
- (1965) Materials Research and Standards , vol.5 , pp. 422
- Johnson, H.H.¹

39
- 0042833500
- Calibrating the Electrical Potential Method for Studying Slow Crack Growth
- (1966) Materials Research and Standards , vol.6 , Issue.8 , pp. 392-394
- Li¹ Wei, R.P.²

40
- 84932576950
- G. A. Miller, S. J. Hudak and R. P. Wei. The Influence of Loading Variables on Environment Enhanced Fatigue Crack Growth in High Strength Steels, Submitted to the Journal of Materials, ASTM (1972).

41
- 84932509135
- Unpublished results.

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.