Failures at Attachment Holes in Brittle Matrix Laminates

Journal of Composite Materials

Volumn 33, Issue 17, 1999, Pages 1600-1619

  Genin, Guy M ^a   Hutchinson, John W ^a  

^a HARVARD UNIVERSITY   (United States)

Author keywords

"Ductile" ceramic matrix composites; Bolt loaded hole; Failure loads; Failure mechanisms; Mechanical attachments; Stress redistribution due to matrix cracking

Indexed keywords

EID: 0007805305     PISSN: 00219983     EISSN: None     Source Type: Journal    
DOI: 10.1177/002199839903301702     Document Type: Article

References (22)

1. G. M. Genin and J. W. Hutchinson "Composite Laminates in Plane Stress: Constitutive Modeling and Stress Redistribution due to Matrix Cracking," J. Am. Ceram. Soc., 80(5):1245-1255 (1997).
2. J. P. Waszczack and T. A. Cruse. "Failure Mode and Strength Prediction of Anisotropic Bolt Bearing Specimens," J. Compos. Mater., 5:421-423 (1971).
3. M. W. Hyer, E. C. Klang, and D. E. Cooper. "The Effects of Pin Elasticity, Clearance, and Friction on the Stresses in a Pin-Loaded Orthotropic Plate," J. Compos. Mater., 21:190-206 (1987).
4. F.-K. Chang, R. A. Scott, and G. Springer. "Failure Strength of Composite Laminates Containing Pin-Loaded Holes - Method of Solution," J. Compos. Mater., 18:255-278 (1984).
5. W. Bickley. "The Distribution of Stress Round a Circular Hole in a Plate," Phil. Trans. Roy. Soc. A 227:383 (1928).
6. T. De Jong. "Stresses Around Pin-Loaded Holes in Elastically Orthotropic or Isotropic Plates," J. Compos. Mater, 11:313-331 (1977).
7. B. L. Agarwal. "Static Strength Prediction of Bolted Joint in Composite Material," AIAA Journal, 18:1345-1375 (1980).
8. R. E. Rowlands, M. U. Rahman, T. L. Wilkinson, and Y. I. Chang. "Single- and Multiple-Bolted Joints in Orthotropic Materials," Composites, 13:273-278 (1982).
9. K.-D. Zhang and C. E. S. Ueng. "Stresses Around a Pin-Loaded Hole in Orthotropic Plates," J. Compos. Materials, 18:432-446 (1984).
10. S. M. Serabian and D. W. Oplinger. "An Experimental and Finite Element Investigation into the Mechanical Response of 0/90 Pin-Loaded Laminates," J. Compos. Mater., 21:631-649 (1987).
11. F.-K. Chang, R. A. Scott, and G. S. Springer. "Failure Strength of Nonlinearly Elastic Composite Laminates Containing a Pin Loaded Hole," J. Compos. Mater., 18:464-477 (1984).
12. C. M. Cady, A. G. Evans, and K. E. Perry. "Stress Redistribution Around Mechanical Attachments in Ceramic Matrix Composites," to appear in J. Am. Ceramic Soc.
13. M. Y. Tsai and J. Morton. "Stress and Failure Analysis of a Pin-Loaded Composite Plate: An Experimental Study," J. Compos. Mater., 24:1101-1120 (1984).
14. F. L. Matthews, A. A. Roshan, and L. N. Phillips. "The Bolt Bearing Strength of Glass/Carbon Hybrid Composites," Composites, 13:225-227 (1982).
15. J. C. NcNulty and F. W. Zok. "Application of Weakest-Link Fracture Statistics to Fiber-Reinforced Ceramic Matrix Composites," to appear in J. Am. Ceramic Soc. (1997).
16. J. C. McNulty and F. W. Zok. Private communication.
17. G. M. Genin, J. W. Hutchinson, J. C. McNulty, and F. W. Zok. "Shear Characterization of Brittle Matrix Cross-Ply Laminates Using the Iosipescu Shear Test," in preparation.
18. N. A. Fleck. "Compressive Failure of Fiber Composites," Advances in Applied Mechanics, New York: Academic Press, 33:43-119 (1997).
19. B. Budiansky. "On the Theoretical Toughness and Strength of Ceramic Composites," Proceedings of IUTAM Symposium on Fracture of Brittle Disordered Materials: Concrete, Rock, Ceramics, Brisbane, September 20-24 (1993).
20. B. Budiansky and J. C. Amazigo. "Notch Strength of Ceramic Composites: Long Fibers, Stochastics, Short Fibers," Harvard University Solid Mechanics Report MECH-269.
21. D. Beyerle, S. M. Spearing, and A. G. Evans, "Damage Mechanisms and the Mechanical Properties of a Laminated 0/90 Ceramic Matrix Composite," J. Am. Ceram. Soc., 75:3321-3330 (1992).
22. B. Harris, F. A. Habib, and R. G. Cooke, "Matrix Cracking and the Mechanical Behaviour of SiC-CAS Composites," Proc. R. Soc. Lond., 437:109-131 (1992).