Application of microline/grid methods to temperature dependent microscopic deformation and damage in CFRP laminates

Experimental Mechanics

Volumn 37, Issue 2, 1997, Pages 182-187

  Takeda, N ^a   Niizuma, H ^b   Ogihara, S ^c   Kobayashi, A ^c  

^a Ctrl Inst Electron Microscopic R   (Japan)

^b UNIVERSITY OF TOKYO   (Japan)

^c TOKYO UNIVERSITY OF SCIENCE   (Japan)

Author keywords

Crack opening displacement; CRFP; Cross ply laminate; Interlaminar shear deformation; Microgrids; Microlines; Transverse crack

Indexed keywords

EID: 0003177181     PISSN: 00144851     EISSN: None     Source Type: Journal    
DOI: 10.1007/BF02317857     Document Type: Article

References (11)

1. Bailey, J.E., Curtis, P.T., and Parvizi, A., "On the Transverse Cracking and Longitudinal Splitting Behavior of Glass and Carbon Fiber Reinforced Epoxy Cross Ply Laminates and the Effect of Poisson and Thermally Generated Strain," Proc. Royal Soc. London, A., 366, 599-623 (1979).
2. Takeda, N. and Ogihara, S., "In-Situ Observation and Probabilistic Prediction of Microscopic Failure Processes in CFRP Cross-Ply Laminates," Comp. Sci. Tech., 52 183-195 (1994).
3. Takeda, N. and Ogihara, S., "Initiation and Growth of Delamination from the Tips of Transverse Cracks in CFRP Cross-Ply Laminates," Comp. Sci. Tech., 52, 309-318 (1994).
4. Hashin, Z., "Analysis of Cracked Laminates: A Variational Approach," Mechanics of Materials, 4, 121-136 (1985).
5. Nairn, J.A., "The Strain Energy Release Rate of Composite Microcracking: A Variational Approach," J. Comp. Mat., 23, 1106-1129 (1989).
6. Lee, J.W., Allen, D.H., and Harris, C.E., "Internal State Variable Approach for Predicting Stiffness Reductions in Fibrous Laminated Composites with Matrix Cracks," J. Comp. Mat., 23 1273-1291 (1989).
7. McCartney, L.N., "Theory of Stress Transfer in a 0°-90°-0° Cross-ply Laminate Containing a Parallel Array of Transverse Cracks," J. Mech. Phys. Solids, 40, 27-68 (1992).
8. Daniel, I.M., Lee, J.W., and Yaniv, G., "Damage Development and Property Degradation in Composite Materials," Mechanics of Composite Materials, AMD, 92, eds. G.J. Dvorak and N. Laws, 149-160 (1988).
9. Flaggs, D.L., "Prediction of Tensile Matrix Failure in Composite Laminates," J. Comp. Mat., 19, 29-50 (1985).
10. Yuan, F.G. and Serek, M.C., "Transverse Cracking and Stiffness Reduction in Comosite Laminates," J. Reinforced Plastics and Composites, 12, 987-1015 (1993).
11. Takeda, N., Niizuma, H., Ogihara, S., and Kobayashi, A., "Experimental Determination of Thermal Residual Stress in CFRP Cross-Ply Laminate," Mat. Sys., 14, 73-78 (1995) (in Japanese).