Effects of Thiosulfate on Susceptibility of Type 316 Stainless Steel to Stress Corrosion Cracking in 3.5% Aqueous Sodium Chloride

Corrosion (Houston)

Volumn 53, Issue 8, 1997, Pages 612-616

  Ashour, E A ^c   Abd El Meguid, E A ^a   Ateya, B G ^b  

^a NATIONAL RESEARCH CENTRE   (Egypt)

^b CAIRO UNIVERSITY   (Egypt)

^c NONE

Author keywords

Chloride; Fracture; Industrial environments; Pitting potential; Stress; Stress corrosion cracking; Thiosulfate; Time to failure; Type 316 stainless steel; Waste water

Indexed keywords

EID: 0001662379     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3290293     Document Type: Article

References (24)

1. R.M. Latanision, R.W. Staehle, in Fundamental Aspects of Stress Corrosion Cracking, eds. R.W. Staehle, A.J. Forty, D. Van Rooyen (Houston, TX: NACE, 1969), p. 214.
2. R.C. Newman, A. Mehta, in Environment-Induced Cracking of Metals, eds. R.P. Gangloff, M.B. Ives (Houston, TX: NACE, 1990).
3. R. Nishimura, Corros. Sci. 34 (1993): p. 1,859.
4. J.K. Lee, Z. Szklarska-Smialowska, Corrosion 44 (1988): p. 560.
5. J. Congleton, W. Yang, Corros. Sci. 37 (1995): p. 429.
6. E.P. Ford, in Corrosion Processes, ed. R.N. Parkins (London, U.K.: Applied Science Publishers, 1982), p. 271.
7. I.J. Yang, Corrosion 49 (1993): p. 576.
8. J.T. Ho, G.P. Yu, Corrosion 48 (1992): p. 147.
9. S.J. Mulford, D. Tromans, Corrosion 44 (1992): p. 891.
10. W.T. Tsai, M.-J. Sheu, J.-T. Lee, Corros. Sci. 38 (1996): p. 33.
11. D. Tromans, L. Frederick, Corrosion 40 (1984): p. 633.
12. H.S. Isaacs, B. Vyas, M.W. Kendig, Corrosion 38 (1982): p. 130.
13. R.C. Newman, K. Sieradzki, H.S. Isaacs, Metall. T-A 13 (1982): p. 2,015.
14. G. Cragnolino, D.D. Macdonald, Corrosion 38 (1982): p. 406.
15. R.C. Newman, W.P. Wong, H. Ezuber, A. Garner, Corrosion 45 (1989): p. 282.
16. D.B. Wells, J. Stewart, R. Davidson, P.M. Scott, D.E. Williams, Corros. Sci. 33 (1992): p. 39.
17. R.P. Frankenthal, H.W. Pickering, J. Electrochem. Soc. 1,199 (1972): p. 1,304.
18. B.F. Brown, C.T. Fujii, E.P. Dahlberg, J. Electrochem. Soc. 116 (1969): p. 218.
19. H.W. Pickering, R.P. Frankenthal, J. Electrochem. Soc. 119 (1972): p. 1,297.
20. Z. Szklarska-Smialowska, Pitting Corrosion of Metals (Houston, TX: NACE, 1986), p. 218.
21. R.J. Biernat, R.G. Robins, Electrochim. Acta 14 (1969): p. 809.
22. Z.A. Iofa, V.V. Batrakov, Cho-Ngok-Ba, Electrochim. Acta 9 (1964): p. 1,645.
23. H.J. Engell, N.D. Stolica, Z. Phys. Chem., NF 20 (1959): p. 113.
24. G. Herbsleb, H.J. Engell, Werkst. Korros. 17 (1966): p. 365.