Crevice Corrosion of Austenitic Alloys in High-Temperature Water

Corrosion

Volumn 54, Issue 9, 1998, Pages 700-712

  Saito, N ^a   Sakamoto, H ^a   Sugimoto, K ^b  

^a TOSHIBA CORPORATION   (Japan)

^b TOHOKU UNIVERSITY   (Japan)

Author keywords

Alloy 600; Chromium; Corrosion potential; Crevice corrosion; High temperature water; Intergranular stress corrosion cracking; Nickel; Oxide films; pH; Type 304 stainless steel; Weight loss

Indexed keywords

CHROMIUM; CRACKS; NICKEL ALLOYS; NICKEL COMPOUNDS; PH; STAINLESS STEEL; STRESS CORROSION CRACKING; SURFACES; WATER;

AUSTENITIC ALLOYS; CORROSION POTENTIAL; CREVICE CORROSION; HIGH TEMPERATURE WATER; INTERGRANULAR STRESS CORROSION CRACKING; OXIDE FILMS; WEIGHT LOSS;

CORROSION RESISTANT ALLOYS;

EID: 0001644108     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3284889     Document Type: Article

References (27)

1. R.A. Page, Corrosion 39 (1983): p. 409.
2. A. Macminn, R.A. Page, Corrosion 44 (1988): p. 239.
3. J. Kuniya, M. Fukai, I. Masaoka, "Hydrogen-Induced Cracking in Cold-Worked, Crevices Typed 304 Austenitic Stainless Steel," Proc. 3rd Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 1987), p. 383.
4. K.S. Brown, G.M. Gordon, "Effects of BWR Coolant Chemistry on the Propensity for IGSCC Intitaion and Growth in Creviced Reactor Internal Components," Proc. 3rd Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors (Houston, TX: NACE, 1987), p. 243.
5. D.F. Taylor, Corrosion 35 (1979): p. 551.
6. D.F. Taylor, M. Silverman, Corrosion 36 (1980): p. 544.
7. D.F. Taylor, C.A. Caramihas, J. Electrochem. Soc. 129 (1982): p. 2,458.
8. D.F. Taylor, C.A. Caramihas, "High-Temperature Aqueous Crevice Corrosion in Alloy 600 and 304L Stainless Steel," in Embrittlement by Localized Crack Environment, ed. R.P. Gangloff (Warrendale, PA: Metallurgical Society of AIME, 1984), p. 105.
9. D.F. Taylor, C.A. Caramihas, "Potential/pH Conditions in Occluded Cells at 288°C," in Corrosion-Assisted Cracking of Stainless and Low-Alloy Steel in LWR Environments, EPRI NP-5064S (Palo Alto, CA: EPRI, 1987).
10. M.G. Fontana, N.D. Greene, Corrosion Engineering, 2nd ed. (New York, NY: MacGraw-Hill, 1978), p. 39.
11. D.A. Vermilyea, "A Film Rupture Model for Stress Corrosion Cracking," in Stress Corrosion Cracking and Hydrogen Embrittlement of Iron-Based Alloys, ed. R.W. Staehle, et al. (Houston, TX: NACE, 1977), p. 208.
12. E.L. Hall, C.L. Briant, Metall. Trans. A. 16A (1985): p. 1,225.
13. S.M. Bruemmer, B.W. Arey, L.A. Charlot, Corrosion 48 (1992): p. 42.
14. G.S. Was, H.H. Tishner, R.M. Latanision, Metall. Trans. A. 12A (1981): p. 1,397.
15. G.S. Was, R.M. Kruger, Acta. Metall. 33 (1985): p. 841.
16. Y. Kanazawa, M. Tsubota, "Stress Corrosion Cracking of Cold-Worked Stainless Steel in High-Temperature Water," CORROSION/94, paper no. 237 (Houston, TX: NACE, 1994).
17. G. Nakayama, M. Akashi, "Stress-Corrosion Cracking Inisitation Process for Alloy 182 Weld Metal in Simulated BWR Environments," CORROSION/95, paper no. 406 (Houston, TX: NACE, 1995).
18. K. Tachibana, T. Masuda, H. Shimizu, S. Miyazaki, M. Yokoi, "A New Pressure-Balanced Outer Reference Electrode Made of Zircalloy Tube Sheath for Corrosion Study of Metals in High-Temperature Aqueous Solutions and Its Application," Proc. 4th Asian-Pacific Corrosion Control Conf., Tokyo, Japan, May 26-31, 1985 (Tokyo, Japan: JSCE, 1985), p. 1.275.
19. M. Hishida, T. Kawakubo, Y. Yamashina, H. Hirayama, Toshiba Review (Spring, 1985): p. 13.
20. R.S. Greeley, W.T. Smith, Jr., R.W. Stoughton, M.H. Lietzke, J. Phys. Chem. 64 (1960): p. 652.
21. L.W. Niedrach, J. Electrochem. Soc. 127 (1980): p. 2,122.
22. L.W. Niedrach, W.H. Stoddard, Corrosion 41 (1985): p. 45.
23. W.L. Marshall, E.U. Frank, "An Equation for the Iron Product of Water at 0°C to 1,000°C and 1 to 10,000 Bars," in Water and Steam, Their Properties and Current Industrial Applications," eds. J. Strab, K. Scheffler (New York, NY: Pergamon Press, 1980), p. 506.
24. C.M. Criss, J.W. Cobble, J. Amer. Chem. Soc. 86 (1964): p. 5,385.
25. D.F. Taylor, J. Electrochem. Sci. 125 (1978): p. 808.
26. Y. Hemmi, N. Ichikawa, N. Saito, T. Masuda, J. Nucl. Sci. Technol. 31 (1994): p. 552.
27. M.E. Indig. Corrosion 47 (1991): p. 203.