Corrosion Potential Behavior of Noble Metal-Modified Alloys in High-Temperature Water

Corrosion

Volumn 52, Issue 10, 1996, Pages 738-743

  Kim, Y J ^a   Niedrach, L W ^a   Andresen, P L ^a  

^a GE GLOBAL RESEARCH   (United States)

Author keywords

Alloy 600; Electrochemical corrosion potential; High temperature water; Hydrogen; Hydrogen peroxide; Low alloy steel; Noble metals; Oxygen; Type 304 stainless steel

Indexed keywords

ALLOYING; CATALYST ACTIVITY; COMPOSITION EFFECTS; CORROSION PROTECTION; ELECTROCHEMICAL CORROSION; HYDROGEN; HYDROGEN PEROXIDE; OXYGEN; PALLADIUM; PLATINUM; STAINLESS STEEL; STRESS CORROSION CRACKING;

CATALYTIC EFFICIENCY; ELECTROCHEMICAL CORROSION POTENTIAL; INTERGRANULAR STRESS CORROSION CRACKING PROTECTION (IGSCC); STAINLESS STEEL 304;

STEEL CORROSION;

EID: 0000772369     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3292066     Document Type: Article

References (15)

1. P.L. Andresen, F.P. Ford, Mater. Sci. Eng. A103 (1988): p. 167.
2. P.L. Andresen, F.P. Ford, S.M. Murphy, J.M. Perk, "State of Knowledge of Radiation Effects on Environmental Cracking in Light-Water Reactor Core Materials," Proc. 4th Int. Symp. Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors [Houston, TX: NACE, 1990), p. 1-83.
3. M.E. Indig, G.M. Gordon, R.B. Davis, "Mitigation of Stress Corrosion Cracking Through Suppression of Radilytic Oxygen," Proc. 1st Int. Symp Environmental Degradation of Materials - Water Reactors (Houston, TX: NACE, 1983), p. 506.
4. L.W. Niedrach, Corrosion 47, 3 (1991): p. 162.
5. P.L. Andresen, L.W. Niedrach, U.S. patent no. 5135709 (1991).
6. Y.J. Kim, L.W. Niedrach, U.S. patent no. 5164152 (1992).
7. L.W. Niedrach, J. Electrochemical Soc. 129 (1982): p. 1,445.
8. C. Wagner, W. Traud, Z. Electrochem. 44 (1938): p. 391.
9. L.W. Niedrach, W.H. Stoddard, Corrosion 42 (1986): p. 696.
10. M. Itow, A. Sudo, M. Yajima, Corrosion 46 (1990): p. 934.
11. C.C. Lin, F.R. Smith, N. Ichikawa, M. Ito, Corrosion 48 (1992): p. 16.
12. D.D. Macdonald, Corrosion 48 (1992): p. 194.
13. J. O'M. Bockris, A.K.N Reddy, Modern Electrochemistry, vol. 2 (New York, NY: Plenum Press, 1973).
14. J.O'M. Bockris, S.U.M. Khan, Surface Electrochemistry (New York, NY: Plenum Press, 1993).
15. P.T.H.M. Verhallen, L.T.P. Oomen, A.J.J.M. v.d. Elsen, A.J. Kruger, Chem. Eng. Sci. 39 (1984): p. 1,535.